High Quality Hard Chrome Plated Piston Rod, Hollow Piston Rod For Shock Absorbers
The piston rod is mainly used in hydraulic pneumatic, engineering machinery, automobile manufacture with the piston rod, guide pillar plastic machinery, packaging machinery, printing machinery, roller, textile machinery, transportation machinery with axis, and linear motion with the linear optical axis.
The piston rod is hard chromium plating on a steel substrate surface coated with a thick layer of chromium plating and its thickness is commonly 10 to 30 microns, using the characteristics of chromium improves parts’ performance, such as hardness, wear resistance, heat resistance and corrosion resistant.
The process features of hard chrome plated piston rod:
1) the cathode current efficiency is as high as 25% ~ 35%, and the deposition rate is very fast.
2) high hardness (900 ~ 1200HV), uniform and dense network cracks, and good abrasion resistance; Microcracks can be produced, and the number of microcracks can reach 800-2000 pieces/cm (according to the need), and improve the anti-corrosion ability.
3) good dispersion ability of the plating bath, uniform thickness of the coating, not easy to produce the phenomenon of rough blister tumor, and the appearance of chromium layer is bright and smooth;
4) the coating has strong bonding strength with the substrate, and the pretreatment is similar to the traditional technology, and
the operation is easier than the traditional process;
5) the content of trivalent chromium in the bath is allowed to be wide, and it usually does not need to discontinue electrolysis for trivalent chromium;
6) the plating solution contains no fluoride, no rare earth elements, and no corrosion of the workpiece without low power.
Detailed Product Description
1. Material: 42CrMo4, 40Cr, CK45,ST52, 20MnV6
2. Tensile strength: Not less than 610 N/MM2
3. Yield strength: Not less than 355 N/MM2
4. Length: 1000mm - 8000mm
5. Diameter: 6mm - 1000mm
6. Advanced inspection apparatus
7. Complete manufactured equipment
Detailed Description
1.CHEMICAL COMPOSITION
| Material | C% | Mn% | Si% | S% | P% | V% | Cr% |
| Ck45 | 0.42-0.50 | 0.50-0.80 | 0.04 | 0.035 | 0.035 | | |
| ST52 | 0.22 | 1.6 | 0.55 | 0.035 | 0.04 | | |
| 20MnV6 | 0.16-0.22 | 1.30-1.70 | 0.10-0.50 | 0.035 | 0.035 | 0.10-0.20 | |
| 42CrMo4 | 0.38-0.45 | 0.60-0.90 | 0.15-0.40 | 0.03 | 0.03 | | 0.90-1.20 |
| 40Cr | 0.37-0.45 | 0.50-0.80 | 0.17-0.37 | | | | 0.80-1.10 |
2.MECHANCIAL PROPERTIES
| Material | T.S N/MM2 | Y.S N/MM2 | E%(MIN) | CHARPY | CONDITION |
| CK45 | 610 | 355 | 15 | >41J | NORMALIZE |
| CK45 | 800 | 630 | 20 | >41J | Q + T |
| ST52 | 500 | 355 | 22 | | NORMALIZE |
| 20MnV6 | 750 | 590 | 12 | >40J | NORMALIZE |
| 42CrMo4 | 980 | 850 | 14 | >47J | Q + T |
| 40Cr | 1000 | 800 | 10 | | Q + T |
3. SUPPLY CONDITION
Ground and chrome plated
4. CHROME THICKNESS
20 to 30 micron
5. SURFACE ROUGHNESS
Ra≤0.2 micron and Rt≤2 micro
6. TOLERANCES ON DIA
ISO f7 on the diameter
7.OVALITY
Half of the tolerance ISO f7
8. STRAIGHTNESS
≤0.2MM/M
9. SURFACE HARDNESS
850-1150HV (vickers 100g)
10.COHESION
No cracks,breaking or detaching after thermic shock(warming up at 300 celsius degrees and cooling
in water)
11 .POROSITY
Test according to ISO 1456/1458 and result yaluation according to ISO 4540 rating 8-10
12 CORROSION RESISTANCE
Test in natural salt spray according to ASTM B 117-72hours
Results evaluation according to ISO 4540 RATING 7-10
13. WELDABILITY
Good
14. PACKING
Anti rust oil to be applied on material and each rod to be packed in paper sleeve
15. CERTIFICATE
All certificate related with material heat treatment and plating is required
Product Tags:
|
|
Hard Chrome Plated Hollow Piston Rod 6mm Stainless Steel For Shock Absorbers Images
|